PC+ABS Bayblend T65 XF Easy Flowing,Covestro Distributor,Low Price

Eigenschaft

Prüfbedingung

Einheit

Norm

typischer Wert

C

Melt volume-flow rate

260℃/5kg

cm³/10 min

ISO 1133

18

Melt viscosity

1000 s-1/ 260 °C

Pa.s

b.o. ISO 11443-A

200

Molding shrinkage, parallel

150x105x3 mm/ 260 °C / MT 80 °C

%

b.o. ISO 2577

0.5-0.7

Molding shrinkage, normal

150x105x3 mm/ 260 °C / MT 80 °C

%

b.o. ISO 2577

0.5-0.7

Eigenschaft

Prüfbedingung

Einheit

Norm

typischer Wert

C

Tensile modulus

1 mm/min

MPa

ISO 527-1,-2

2350

C

Yield stress

50 mm/min

MPa

ISO 527-1,-2

54

C

Yield strain

50 mm/min

%

ISO 527-1,-2

4.4

Stress at break

50 mm/min

MPa

ISO 527-1,-2

47

Stress at break

50 mm/min

%

ISO 527-1,-2

>50

Flexural modulus

2 mm/min

MPa

ISO 178

2350

Flexural stress at 3.5 % strain

2 mm/min

MPa

ISO 178

73

Flexural strength

2 mm/min

MPa

ISO 178

84

Izod impact strength

23°C

kJ/m²

ISO 180/U

N

Izod impact strength

-30 °C

kJ/m²

ISO 180/U

N

Izod notched impact strength

23 °C

kJ/m²

ISO 180/A

48

Izod notched impact strength

-30 °C

kJ/m²

ISO 180/A

35

C

Charpy notched impact strength

23 °C

kJ/m²

ISO 179/1eA

50

C

Charpy notched impact strength

-30 °C

kJ/m²

ISO 179/1eA

36